MECHANICAL PROPERTIES

Notation

A = % elongation at fracture
R eH = ReH Minimum Yield strength ( MPa )
R p0,2 = 0,2 % proof strength ( MPa )
Rm = Tensile strength ( MPa )
HV = Hardness value (Vickers)
t = Product thickness for specified properties ( mm)
+N = normalised
+NT = normalised and tempered
+QT = quenched and tempered
C = Cold rolled.
H = Hot rolled strip
P = Hot rolled plate
FN = (Deoxidation method) Rimming steels not permitted
FF = (Deoxidation method)Fully killed steel







BS EN 10025-2 Hot rolled products of non-alloy structural steels
Technical delivery conditions for non-alloy structural steels





Product Chemical composition

Name Number Deoxidation Method C % For thickness range Si max Mn max P max S max N max Cu max Other
  =< 16 > 16
=<40
>40 % % % % % % %
S235JR 1.0038 FN 0,19 0,19 0,23 - 1,5 0,045 0,045 0,014 0,60 -
S235JO 1.0114 FN 0,19 0,19 0,19 - 1,5 0,040 0,040 0,014 0,60 -
S235J2 1.0117 FF 0,19 0,19 0,19 - 1,5 0,035 0,035 - 0,60 -
S275JR 1.0044 FN 0,24 0,24 0,25 - 1,6 0,045 0,045 0,014 0,60 -
S275JO 1.0143 FN 0,21 0,21 0,21 - 1,6 0,040 0,040 0,014 0,60 -
S275J2 1.0145 FF 0,21 0,21 0,21 - 1,6 0,035 0,035 - 0,60 -
S355JR 1.0045 FN 0,27 0,27 0,27 0,60 1,7 0,045 0,045 0,014 0,60 -
S355J0 1.0553 FN 0,23 0,23 0,24 0,60 1,7 0,040 0,040 0,014 0,60 -
S355J2 1.0577 FF 0,23 0,23 0,24 0,60 1,7 0,035 0,035 - 0,60 -
S355K2 1.0596 FF 0,23 0,23 0,24 0,60 1,7 0,035 0,035 - 0,60 -
S450J0 1.0590 FF 0,23 0,23 0,24 0,60 1,8 0,04 0,04 0,027 0,60 -


Basic mechanical properties at room temperature

Name Number ReH Minimum Yield strength (MPa )
for nominal thickness(mm)
R m (MPa)
for nominal thickness (mm)
<16 =>16 >40 >63 >80 >100 >150 >200 >250 <3 =>3 >100 >150 >250
  =< 40 =< 63 =< 80 =< 100 =< 150 =< 200 =< 250 =< 400   =< 100 =< 150 <= 250 =< 400
S235JR 1.0038 235 225 215 215 215 195 185 175 - 360-510 360-510 350-500 340-490  
S235JO 1.0114 235 225 215 215 215 195 185 175 - 360-510 360-510 350-500 340-490  
S235J2 1.0117 235 225 215 215 215 195 185 175 165 360-510 360-510 350-500 340-490 330-480
S275JR 1.0044 275 265 255 245 235 225 215 205   430-580 410-560 400-540 380-540  
S275JO 1.0143 275 265 255 245 235 225 215 205 - 430-580 410-560 400-540 380-540  
S275J2 1.0145 275 265 255 245 235 225 215 205 195 430-580 410-560 400-540 380-540 380-540
S355JR 1.0045 355 345 335 325 315 295 285 275 - 510-680 470-630 450-600 450-600  
S355J0 1.0553 355 345 335 325 315 295 285 275 - 510-680 470-630 450-600 450-600  
S355J2 1.0577 355 345 335 325 315 295 285 275 265 510-680 470-630 450-600 450-600 450-600
S355K2 1.0596 355 345 335 325 315 295 285 275 265 510-680 470-630 450-600 450-600 450-600
S450J0 1.0590 450 430 410 390 380 380 - - - - 550-720 530-700 - -





BS EN 10025-3 :Hot rolled products of non-alloy structural steels
Technical delivery conditions for normalized/normalized rolled weldable fine grain structural steels




Product Chemical composition



Name Number C max Si max Mn max        P max S max Nb max V max Al tot Ti max Cr max Ni max Mo max Cu max vN max
% % % % % % % % % % % % % %
S275N 1.0490 0,20 0,45 0,45-1,60 0,035 0,030 0,060 0,070 0,015 0,060 0,35 0,35 0,13 0,60 0,017
S275NL 1.0491 0,18 0,45 0,45-1,60 0,030 0,025 0,060 0,070 0,015 0,060 0,35 0,35 0,13 0,60 0,017
S355N 1.0545 0,22 0,55 0,85-1,75 0,035 0,030 0,060 0,14 0,015 0,060 0,35 0,55 0,13 0,60 0,017
S355NL 1.0546 0,20 0,55 0,85-1,80 0,030 0,025 0,060 0,14 0,015 0,060 0,35 0,55 0,13 0,60 0,017
S420N 1.8902 0,22 0,65 0,95-1,80 0,035 0,030 0,060 0,22 0,015 0,060 0,35 0,85 0,13 0,60 0,027
S420NL 1.8912 0,22 0,65 0,95-1,80 0,030 0,025 0,060 0,22 0,015 0,060 0,35 0,85 0,13 0,60 0,027
S460N 1.8901 0,22 0,65 0,95-1,80 0,035 0,030 0,060 0,22 0,015 0,060 0,35 0,85 0,13 0,60 0,027
S460NL 1.8903 0,22 0,65 0,95-1,80 0,030 0,025 0,060 0,22 0,015 0,060 0,35 0,85 0,13 0,60 0,027


Basic mechanical properties at room temperature

Name Number R eH Minimum Yield strength (MPa)
for nominal thickness(mm)
R m (MPa)
for nominal thickness (mm)
A -
Elongation(min)
<16 >16 >40 >63 >80 >100 >150 >200 <100 >100 >200
  =< 40 =< 63 =< 80 =< 100 =< 150 =< 200 =< 250   =< 200 =< 250 %
S275N 1.0490 275 265 255 245 235 225 215 205 370-510 350-480 350-480 23-24
S275NL 1.0491 275 265 255 245 235 225 215 205 370-510 350-480 350-480 23-24
S355N 1.0545 355 345 335 325 315 295 285 275 470-630 450-600 450-600 21-22
S355NL 1.0546 355 345 335 325 315 295 285 275 470-630 450-600 450-600 21-22
S420N 1.8902 420 400 390 370 360 340 330 320 520-680 500-650 500-650 18-19
S420NL 1.8912 420 400 390 370 360 340 330 320 520-680 500-650 500-650 18-19
S460N 1.8901 460 440 430 410 400 380 370 - 540-720 530-710 - 17
S460NL 1.8903 460 440 430 410 400 380 370 - 540-720 530-710 - 17





BS EN 10025-4 :Technical delivery conditions for thermomechanical rolled weldable fine grain structural steels



Product Chemical composition

Name Number C max Si max Mn max P max S max Nb max V max Al tot Ti max Cr max Ni max Mo max Cu max N max
% % % % % % % % min % % % % % %
S275M 1.8818 0,15 0,55 1,60 0,035 0,030 0,06 0,10 0,015 0,06 0,35 0,35 0,13 0,60 0,17
S275ML 1.8819 0,15 0,55 1,60 0,030 0,025 0,06 0,10 0,015 0,06 0,35 0,35 0,13 0,60 0,17
S355M 18823 0,16 0,55 1,70 0,035 0,030 0,06 0,12 0,015 0,06 0,35 0,55 0,13 0,60 0,17
S355ML 1.8834 0,16 0,55 1,70 0,030 0,025 0,06 0,12 0,015 0,06 0,35 0,55 0,13 0,60 0,17
S420M 18825 0,18 0,55 1,80 0,035 0,030 0,06 0,14 0,015 0,06 0,35 0,85 0,23 0,60 0,27
S420ML 1.8836 0,18 0,55 0,17 0,030 0,025 0,06 0,14 0,015 0,06 0,35 0,85 0,23 0,60 0,27
S460M 18827 0,18 0,65 0,17 0,035 0,030 0,06 0,14 0,015 0,06 0,35 0,85 0,23 0,60 0,27
S460ML 1.8838 0,18 0,65 1,80 0,030 0,025 0,06 0,14 0,015 0,06 0,35 0,85 0,23 0,60 0,27



Basic mechanical properties at room temperature

Name Number R eH Minimum Yield strength (MPa)
for nominal thickness(mm)
Rm (MPa)
for nominal thickness (mm)
A.
Elongation (min)
<16 >16 >40 >63 >80 >100 <=40 >40 >63 >80 >100
  =< 40 =< 63 =< 80 =< 100 =< 120   =<63 =<80 =<80 =<120 %
S275M 1.8818 275 265 255 245 245 240 370-530 360-520 350-510 350-510 350-510 24
S275ML 1.8819 275 265 255 245 245 240 370-530 360-520 350-510 350-510 350-510 24
S355M 18823 355 345 335 325 325 320 470-630 450-610 440-600 440-600 430-590 22
S355ML 1.8834 355 345 335 325 325 320 470-630 450-610 440-600 440-600 430-590 22
S420M 18825 420 400 390 380 370 365 520-680 500-660 480-640 470-630 460-620 19
S420ML 1.8836 420 400 390 380 370 365 520-680 500-660 480-640 470-630 460-620 19
S460M 18827 460 440 430 410 400 385 540-720 530-710 510-690 500-680 490-660 17
S460ML 1.8838 460 440 430 410 400 385 540-720 530-710 510-690 500-680 490-660 17





BS EN 10025-5 :Technical delivery conditions for structural steels with improved atmospheric corrosion resistance



Product Chemical composition

Deoxidation Method
FN = Rimming steels not permitted
FF = Fully killed steel

Name Number Method;
of
Deoxidation
C Si Mn P S N Cr Cu others
max % max % % % max % max % % %  
S235J0W 1.8958 FN 0,16 0,45 0,15-0,70 max0,040 0,040 0,010 0,35-0,85 0,20-0,60 Ni max 0,70
S235J2W 1.8961 FF 0,16 0,45 0,15-0,70 max0,040 0,035 0,010 0,35-0,85 0,20-0,60 Ni max 0,70
S355J0WP 1.8945 FN 0,15 0,80 max 1,1 0,05-0,16 0,040 0,010 0,25-1,35 0,20-0,60 Ni max 0,70
S355J2WP 1.8946 FF 0,15 0,80 max 1,1 0,05-0,16 0,035 0,010 0,25-1,35 0,20-0,60 Ni max 0,70
S355J0W 1.8959 FN 0,19 0,55 0,45-1,6 max 0,040 0,040 0,010 0,35-0,85 0,20-0,60 Ni max 0,70
S355J2W 1.8965 FF 0,19 0,55 0,45-1,6 max 0,035 0,035 0,010 0,35-0,85 0,20-0,60 Ni max 0,70
S355K2W 1.8967 FF 0,19 0,50 0,45-1,6 max 0,035 0,035 0,010 0,35-0,85 0,20-0,60 Ni max 0,70



Basic mechanical properties at room temperature

Name Number R eH Minimum Yield strength (MPa)
for nominal thickness(mm)
Rm (MPa)
for nominal thickness (mm)
A
Elongation (min)
<16 >16 >40 >63 >80 >100 <3 >3 >100
  =< 40 =< 63 =< 80 =< 100 =< 150   =<100 =< 150 %
S235J0W 1.8958 235 225 215 215 215 195 360-510 360-510 350-500 19-22
S235J2W 1.8961 235 225 215 215 215 195 360-510 360-510 350-500 17-22
S355J0WP 1.8945 355 345 - -     510-680 470-630 - 16-22
S355J2WP 1.8946 355 345 - -     510-680 470-630 - 14-20
S355J0W 1.8959 355 345 335 325 315 295 510-680 470-630 450-600 16-22
S355J2W 1.8965 355 345 335 325 315 295 510-680 470-630 450-600 14-20
S355K2W 1.8967 355 345 335 325 315 295 510-680 470-630 450-600 14-20






BS EN 10025-6 :Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition



Product Chemical composition

Quality C Si Mn P S N B Cr Cu Mo Nb Ni Ti V Zr
  max % max % max % max % max % max % max % max % max % max % max % max % max % max % max %
No symbo; 0,22 0,86 1,8 0,030 0,017 0,016 0,006 1,60 0,055 0,74 0,07 2,1 0,07 0,14 0,17
L 0,22 0,86 1,8 0,025 0,012 0,016 0,006 1,60 0,055 0,74 0,07 2,1 0,07 0,14 0,17
L1 0,22 0,86 1,8 0,025 0,012 0,016 0,006 1,60 0,055 0,74 0,07 2,1 0,07 0,14 0,17



Basic mechanical properties at room temperature

Name Number R eH Minimum Yield strength (MPa)
for nominal thickness(mm)
Rm (MPa)
for nominal thickness (mm)
A
Elongation min )
=> 3 >50 >100 =>3 >50 >100
=< 50 =< 100 =< 150 =< 50 =< 100 =< 150 %
S460Q 1.8908 460 440 400 550-720 550-720 500-670 17
S460QL 1.8906 460 440 400 550-720 550-720 500-670 17
S460QL1 1.8916 460 440 400 550-720 550-720 500-670 17
S500Q 1.8924 500 480 440 590-770 590-770 540-720 17
S500QL 1.8909 500 480 440 590-770 590-770 540-720 17
S500QL1 1.8984 500 480 440 590-770 590-770 540-720 17
S550Q 1.8904 550 530 490 640-820 640-820 590-770 16
S550QL 1.8926 550 530 490 640-820 640-820 590-770 16
S550QL1 1.8986 550 530 490 640-820 640-820 590-770 16
S620Q 1.8914 620 580 560 700-890 700-890 650-830 15
S620QL 1.8927 620 580 560 700-890 700-890 650-830 15
S620QL1 1.8987 620 580 560 700-890 700-890 650-830 15
S690Q 1.8931 690 650 630 770-940 760-930 710-900 14
S690QL 1.8928 690 650 630 770-940 760-930 710-900 14
S690QL1 1.8988 690 650 630 770-940 760-930 710-900 14
S890Q 1.8940 890 830 - 940-1100 880-1100 - 11
S890QL 1.8983 890 830 - 940-1100 880-1100 - 11
S890QL1 1.8925 890 830 - 940-1100 880-1100 - 11
S960Q 1.8941 960 - - 980-1150 - - 10
S960QL 1.8933 960 - - 980-1150 - - 10


High-strength steels for cold-forming, thermomechanically-rolled

Usage

The steel grades of the S315MC to S700MC series are used for cold-formed components of the most varied designs. Their fields of application include the manufacture of:
  • Longitudinal beams
  • Frames
  • Cold-pressed parts
  • Cold-rolled sections
  • Structural pipes
The user of these steel grades must make sure that his calculation, design and processing methods are appropriate for the material. The forming process used must be suitable for the intended application and comply with the state-of-the-art; it is of fundamental importance to the processing behaviour of these steel grades.
These low-perlite steel grades offer excellent bending, flanging, cold-bordering and folding properties in both longitudinal and transverse direction. The bending radii specified below should be observed as minimum values.

Standards

Europe Material no. D F I GB USA Salzgitter Flachstahl FK1)
EN 10149-2   SEW 092 NFA 36-231 UNI 8890 BS 1449 Sec. 1.4 ASTM A 1011/ SAE J 1392    
S315MC 1.0972 - E 315 D - HR 40F30 045 XLK PSQ 32 B
  1.0974 QStE 340 TM - - - HSLAS-F Gr. 50 [340]/050 XLK PSQ 34 B
S355MC 1.0976 - E 355 D Fe E 355 TM HR 43F35 - PSQ 36 B
  1.0978 QStE 380 TM - - HR 46F40 - PSQ 38 B
S420MC 1.0980 QStE 420 TM E 420 D Fe E 420 TM - HSLAS-F Gr. 60 [410]/060 XLK PSQ 42 C
S460MC 1.0982 QStE 460 TM - - HR 50F45 - PSQ 46 C
S500MC 1.0984 QStE 500 TM E 490 D Fe E 490 TM - HSLAS-F Gr. 70 [480]/070 XLK PSQ 50 D
S550MC 1.0986 QStE 550 TM E 560 D Fe E 560 TM - HSLAS-F Gr. 80 [550]/080 XLK PSQ 55 D
S600MC 1.8969 - E 620 D - - - PSQ 60 D
S650MC 1.8976 - - - - - PSQ 65 D
S700MC 1.8974 - E 690 D - - - PSQ 70 D

1) FK = Tensile strength class

The following limitation shall additionally apply to all steel grades:
Nb ≤ 0,09 %, V ≤ 0,20 %, 
with the total of Nb, V and Ti not exceeding 0,22 %.

Smallest bending radius

Grade Smallest recommended bending radius bending angles ≤ 90°
  e1) ≤ 3 3 < e1) < 6 e1) > 6
S315MC 0,25 e 0,5 e 1,0 e
QStE 340 TM 0,25 e 0,5 e 1,0 e
S355MC 0,25 e 0,5 e 1,0 e
QStE 380 TM 0,25 e 0,5 e 1,0 e
S420MC 0,5 e 1 ,0 e 1,5 e
S460MC 0,5 e 1,0 e 1,5 e
S500MC 1,0 e 1,5 e 2,0 e
S550MC 1,0 e 1,5 e 2,0 e
S600MC 1,0 e 1,5 e 2,0 e
S650MC 1,5 e 2,0 e 2,5 e
S700MC 1,5 e 2,0 e 2,5 e

1) Nominal thickness e [mm]

Chemical composition in percent by weight [%] (Heat analysis)

Grade  C Si Mn P S 1) Altotal Mo Ti B
  max. max. max. max. max. min. max. max. max.
S315MC 0,12 0,50 1,30 0,025 0,020 0,015 - 0,15 -
QStE 340 TM 0,12 0,50 1,30 0,025 0,010 0,015 - - -
S355MC 0,12 0,50 1,50 0,025 0,020 0,015 - 0,15 -
QStE 380 TM 0,12 0,50 1,50 0,025 0,010 0,015 - - -
S420MC 0,12 0,50 1,60 0,025 0,015 0,015 - 0,15 -
S460MC 0,12 0,50 1,60 0,025 0,015 0,015 - 0,15 -
S500MC 0,12 0,50 1,70 0,025 0,015 0,015 - 0,15 -
S550MC 0,12 0,50 1,80 0,025 0,015 0,015 - 0,15 -
S600MC 0,12 0,50 1,90 0,025 0,015 0,015 0,50 0,22 0,005
S650MC 0,12 0,60 2,00 0,025 0,015 0,015 0,50 0,22 0,005
S700MC 0,12 0,60 2,10 0,025 0,015 0,015 0,50 0,22 0,005

1) If agreed in the order, the sulphur content is 0,010 % max.

Mechanical properties1)

Grade Min. yield strength Tensile strength Min. total elongation [%]
  MPa MPa L0 = 80 mm
e2) < 3
L0 = 5,65 √S0
e2) ≥ 3
S315MC 315 390 - 510 20 24
QStE 340 TM 340 420 - 540 19 23
S355MC 355 430 - 550 19 23
QStE 380 TM 380 450 - 590 18 22
S420MC 420 480 - 620 16 19
S460MC 460 520 - 670 14 17
S500MC 500 550 - 700 12 14
S550MC 550 600 - 760 12 14
S600MC 600 650 - 820 11 13
S650MC 6502) 700 - 880 10 12
S700MC 7002) 750 - 950 10 12

1) The tensile test values apply to longitudinal samples for QStE 340 TM and QStE 380 TM in widths
    ≥ 600 mm tensile test values apply to transvers samples.
2) In case the thickness is > 8 mm, the yield strength values may be reduced by 20 MPa.
3) Nominal thickness e [mm]

Notch impact energy

If agreed in the order, the notch impact energy is proved using longitudinal samples at -20 °C. The average notch impact energy from 3 samples must be 40 J minimum. One individual value may fall short of the required minimum value by not more than 30 %. The sample width shall equal the product thickness if the latter is between 5 and 10 mm, the tests being performed using samples which are similar to Charpy-V samples. The required minimum values are to be reduced proportionally to the sample width.

Heat treatment

Normalised and stress relief annealing above 580 °C with long holding times results in a reduction of yield strength and tensile strength as compared to the ‘as-delivered’ condition which is why such heat treatments should be avoided. It also follows that these steel grades are not suitable for hot-forming. If low-voltage annealing is necessary to compensate for the welding stresses, the recommended annealing time between 530 °C and 580 °C is 30 minutes for all product thicknesses and steel grades.

Welding

These steel grades can be welded both manually and using automatic equipment by means of all electrical welding processes provided the general technical rules are observed. No major hardness increases appear in the heat-affected zone. Preheating is not necessary under normal welding conditions and down to workpiece temperatures of +5 °C. Below +5 °C, pre-heating to 150 °C is recommended.

The welding wires and electrodes approved in the respective strength category must be used as filler metals.

In addition to this, the general meaning of the detailed information provided in ‘Stahl-Eisen-Werkstoffblatt’ (Iron and steel material sheet) 088 must be observed.

Condition of delivery, scope of testing and certificate

The provisions of EN 10149-2 shall apply for delivery and inspection. The products are delivered in a thermomechanically-rolled condition.


Inspection & Approval Certificates : C/W Certificate (Calibration Works Certificate) EN10204 3.1 Mill Test Certificate, NACE MR-0175 / ISO 15156, European Pressure Equipment Directive PED-97/23/EC, AD-2000-WO, ASME Boiler & Pressure Vessel Code Sec.II Part A Ed. 2008, API 6A, with 3.2 certificate duly Certified & Approved by LRS (Lloyd's Register), GL (Germanischer Lloyd), BV (Bureau Veritas), DNV (Det Norske Veritas), SGS, TUV, ABS, RINA, IRS, NORSOK Approved


If you have any requirement of above items, please feel free to contact us


Regards,


CONTACT PERSON :

 

 

MUKESH SHAH
Director
Mobile No. 0091 - 9820292499
Email -
marketing@rolexmetals.com


ROLEX METAL DISTRIBUTORS
( A METAL & STEEL Company )
57-A, KHATARGALLI,
THAKURDWAR,
MUMBAI - 400002, INDIA.
TEL.No. 0091-22-23858802
TEL.No. 0091-22-23823963
FAX No. 0091-22-23898724
Email -
marketing@rolexmetals.com
Website –
www.rolexmetals.com

 
 

CHAIRMAN – chairman@rolexmetals.com

MANAGING DIRECTOR – managingdirector@rolexmetals.com

TECHNICAL DIRECTOR – technicaldirector@rolexmetals.com

SALES DIRECTOR – salesdirector@rolexmetals.com

COMMERCIAL DIRECTOR – commercialdirector@rolexmetals.com

 

COMMERCIAL MANAGER – commercial@rolexmetals.com

GENERAL MANAGER – generalmanager@rolexmetals.com

SALES MANAGER – salesmanager@rolexmetals.com

PURCHASE MANAGER – purchasemanager@rolexmetals.com

TECHNICAL MANAGER – technical@rolexmetals.com

WORKS MANAGER – worksmanager@rolexmetals.com

STORES MANAGER – stores@rolexmetals.com

WAREHOUSE MANAGER – warehouse@rolexmetals.com

SALES DOMESTIC – salesdomestic@rolexmetals.com

SALES INTERNATIONAL – salesinternational@rolexmetals.com

SALES GENERAL – sales@rolexmetals.com

PURCHASE GENERAL – purchase@rolexmetals.com

FINANCE MANAGER – finance@rolexmetals.com

ACCOUNTS MANAGER – accounts@rolexmetals.com

GENERAL INFORMATION – info@rolexmetals.com

 

EXPORT MANAGER – export@rolexmetals.com

IMPORT MANAGER – import@rolexmetals.com

AIR EXPORT – airexport@rolexmetals.com

SEA EXPORT – seaexport@rolexmetals.com

CUSTOMS – customs@rolexmetals.com

 

AIR FREIGHT – airfreight@rolexmetals.com

SEA FREIGHT – seafreight@rolexmetals.com

DESPATCH – despatch@rolexmetals.com

INSPECTION – inspection@rolexmetals.com

LOGISTICS – logistics@rolexmetals.com

TRANSPORT – transport@rolexmetals.com

 

KALAMBOLI WAREHOUSE – kalamboli@rolexmetals.com

TALOJA WAREHOUSE – taloja@rolexmetals.com

KHOPOLI WAREHOUSE – khopoli@rolexmetals.com

NHAVA SHEVA WAREHOUSE – nhavasheva@rolexmetals.com

KANDLA WAREHOUSE – kandla@rolexmetals.com

MUMBAI WAREHOUSE – mumbai@rolexmetals.com

STOCKYARD – stockyard@rolexmetals.com

 

SERVICE – service@rolexmetals.com

SUPPORT – support@rolexmetals.com

RECRUITMENT – career@rolexmetals.com

WEBMASTER – webmaster@rolexmetals.com

CUSTOMER CARE – customercare@rolexmetals.com